3DPrinting
3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at: !functionalprint@kbin.social or !functionalprint@fedia.io
There are CAD communities available at: !cad@lemmy.world or !freecad@lemmy.ml
Rules
-
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
-
Be respectful, especially when disagreeing. Everyone should feel welcome here.
-
No porn (NSFW prints are acceptable but must be marked NSFW)
-
No Ads / Spamming / Guerrilla Marketing
-
Do not create links to reddit
-
If you see an issue please flag it
-
No guns
-
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe/ may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
Moderation policy: Light, mostly invisible
view the rest of the comments
That bed temp is too high, past the Tg. You should be able to use 95c for both.
The chamber temp is likely fine, I typically get my chamber to about 45c on my x1c by throwing a blanket over it and it does abs fine. Maybe try throwing a blanket over your enclosure too to get it to that magic 50C.
Is the filament dry? One of the first symptoms you'll see with bad, wet filament is really poor bed adhesion and much higher warpage, even if its not wet enough to cause the typical problems of nozzle foaming and stringing. YMMV but I've found maybe 80% of spools of ASA Ive opened so far end to be "wet" out of the box from multiple manufacturers. So definitely consider drying all your spools before going down any other path.
A smooth plate has better adhesion than a textured plate, if you have one available.
I'll give 95C bed a try, I do have a smooth PEI bed as well so I'll try that one too. Filaments should be dry, but I'll give them another round in the dryer before trying again.
Yeah, it's counterintuitive but too high of a bed temp can cause less adhesion as it makes the first layer plastic underneath too soft. 95 to 100 should be all you need, unless you verify with an external thermocouple that your bed surface runs too cold vs the printer's thermistor.